25.01.2007 Description Scrap HMS1&2 (80:20) and HMS1 (100%) Steel scraps shall be considered free of alloys when the residual alloying elements do not exceed the following percentages: percent Nickel 0.45 Chromium 0.20 Molybdenum 0.10 Manganese 1.65 The combined residuals other than manganese shall not exceed a total of 0.60 percent. ISRI-CODES: 200 No. 1 heavy melting steel. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 60 x 24 inches (charging box size) prepared in a manner to insure compact charging. 201 No. 1 heavy melting steel 3 feet x 18 inches. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 36 inches x 18 inches (charging box size) prepared in a manner to insure compact charging. 202 No. 1 heavy melting steel 5 feet x 18 inches. Wrought iron and/or steel scrap 1/4 inch and over in thickness. Individual pieces not over 60 inches x 18 inches (charging box size) prepared in a manner to insure compact charging. 203 No. 2 heavy melting steel.* Wrought iron and steel scrap, black and galvanized, 1/8 inch and over in thickness, charging box size to include material not suitable as No. 1 heavy melting steel. Prepared in a manner to insure compact charging. 204 No. 2 heavy melting steel.* Wrought iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May include all automobile scrap properly prepared. 205 No. 2 heavy melting steel 3 feet x 18 inches. Wrought iron and steel scrap, black and galvanized, maximum size 36 x 18 inches. May include automobile scrap, properly prepared, however, to be free of sheet iron or thin gauged material. 206 No. 2 heavy melting steel 5 feet x 18 inches. Wrought iron and steel scrap, black and galvanized, maximum size 60 x 18 inches. May include automobile scrap, properly prepared, however, to be free of sheet iron or thin gauged ma Used Rails R 50 – R 65